An Ag based brazing system with a tunable thermal expansion for the use as sealant for solid oxide cells

  • Kiebach, Wolff-Ragnar
  • Engelbrecht, Kurt
  • Grahl-Madsen, Laila
  • Sieborg, Bertil
  • Chen, Ming
  • Hjelm, Johan
  • Norrman, Kion
  • Chatzichristodoulou, Christodoulos
  • Hendriksen, Peter Vang
Publication Date
Jan 01, 2016
Online Research Database In Technology
External links


An Ag-Al2TiO5 composite braze was developed and successfully tested as seal for solid oxide cells. The thermo-mechanical properties of the Ag-Al2TiO5 system and the chemical compatibility between this composite braze and relevant materials used in stacks were characterized and the leak rates as a function of the operation temperature were measured. The thermal expansion coefficient in the Ag-Al2TiO5 system can be tailored by varying the amount of the ceramic filler. The brazing process can be carried out in air, the joining partners showed a good chemical stability and sufficient low leak rates were demonstrated. Furthermore, the long-term stability of the Ag-Al2TiO5 composite braze was studied under relevant SOFC and SOEC conditions. The stability of brazed Crofer/Ag-Al2TiO5/NiO-YSZ assemblies in reducing atmosphere and in pure oxygen was investigated over 500 h at 850 °C. Additionally, a cell component test was performed to investigate the durability of the Ag-Al2TiO5 seal when exposed to dual atmosphere. The seals performed well over 900 h under electrolysis operation conditions (−0.5 A cm2, 850 °C), and no cell degradation related to the Ag-Al2TiO5 sealing was found, indicating that the developed braze system is applicable for the use in SOFC/SOEC stacks.

Report this publication


Seen <100 times