Magnetocaloric properties of LaFe13−x−yCoxSiy and commercial grade Gd

Authors
Publisher
Elsevier BV North-Holland
Publication Date
Keywords
  • The Magnetocaloric Properties Of Three Samples Of Lafe13−X−Ycoxsiy Have Been Measured And Compar
  • The Samples Have (X=0
  • 86
  • Y=1
  • 08)
  • (X=0
  • 94
  • Y=1
  • 01) And (X=0
  • 97
  • Y=1
  • 07) Yielding Curie Temperatures In The Range 276–288 K
  • The Magnetization
  • Specific Heat Capacity And Adiabatic Temperature Change Have Been Measured Over A Broad Temperature
  • Importantly
  • All Measurements Were Corrected For Demagnetization
  • Allowing The Data To Be Directly Compared
  • In An Internal Field Of 1 T The Maximum Specific Entropy Changes Were 6
  • 2
  • 5
  • 1 And 5
  • 0 J/Kg K
  • The Specific Heat Capacities Were 910
  • 840 And 835 J/Kg K And The Adiabatic Temperature Changes Were 2
  • 3
  • 2
  • 1 And 2
  • 1 K For The Three Lafecosi Samples Respectively
  • For Gd In An Internal Field Of 1 T The Maximum Specific Entropy Change Was 3
  • 1 J/Kg K
  • The Specific Heat Capacity Was 340 J/Kg K And The Adiabatic Temperature Change Was 3
  • 3 K
  • The Adiabatic Temperature Change Was Also Calculated From The Measured Values Of The Specific Heat C
  • In General An Excellent Agreement Was Seen

Abstract

Magnetocaloric properties of LaFe13−x−yCoxSiy and commercial grade Gd - DTU Orbit (18/03/14) Magnetocaloric properties of LaFe13−x−yCoxSiy and commercial grade Gd - DTU Orbit (18/03/14) Magnetocaloric properties of LaFe13−x−yCoxSiy and commercial grade Gd Bjørk, R., Bahl, C. R. H. & Katter, M. 2010 In : Journal of Magnetism and Magnetic Materials. 322, 24, p. 3882-3888 Publication: Research - peer-review › Journal article – Annual report year: 2010