Published in Materials
Although called stainless steels, austenitic steels are sensitive to localized corrosion, namely pitting, crevice, and intergranular form. Seventeen grades of steel were tested for localized corrosion. Steels were also tested in general corrosion and in galvanic couplings (steels–precious alloys) used in watchmaking applications. The evaluations ha...
Published in Materials
The biggest obstacle for the application of tungsten as the target materials in the spallation neutron source is its serious corrosion in the coolant of flowing water. For this reason, W–Cr–C clad tungsten was developed by tungsten carburizing in a spark plasma sintering device, with superior corrosion resistance in the static immersion and electro...
Published in Materials
The effect of 0.2 wt.% Zn addition on microstructure, age hardening and intergranular corrosion (IGC) properties of Al-Mg-Si alloy were investigated by scanning electron microscope, transmission electron microscope, hardness testing, and electrochemistry testing. The results showed that the addition of Zn can accelerate the transformation of GP zon...
In this work, influence of ultrasonic nanocrystal surface modification (UNSM) on the degree of sensitization (DOS) in Inconel 718 has been studied and correlated with the resulting microstructure. The UNSM processed samples decreased their grain size from 11.9 µ / m to 7.75 µ / m, increasing the surface of grain boundaries, and thus enhan...
Published in Materials
This study investigated the susceptibility to intergranular corrosion (IGC) in austenitic stainless steel with various degrees of sensitization (DOSs) from a microstructural viewpoint based on the coincidence site lattice (CSL) model. IGC testing was conducted using oxalic acid and type 304 stainless steel specimens with electrochemical potentiokin...
In this paper, a 3D cellular automata approach of intergranular corrosion in presented. A model is proposed, along with experimental results both qualitatively (groove morphology, groove angle distribution) and quantitatively (mass loss, corrosion rate, corrosion front evolution). Simulations have been performed using a new asynchronous algorithm: ...
This paper reports the effects of thermal aging between 650 and 850 ° / C on the localized corrosion behavior of lean duplex stainless steel (LDSS 2404). Critical pitting temperature (CPT) and double loop electrochemical potentiokinetic reactivation (DL-EPR) tests were performed. The localization of pitting attack and intergranular corrosion (IG...
Published in Materials
The intergranular corrosion (IGC) behavior of a new metastable austenitic Cr–Mn–Ni–N–Cu high-strength stainless steel under various heat treatments was studied. The samples were solution treated at 1050 °C for 30 min and then aged at 600 to 900 °C for 10 to 300 min, respectively. The IGC susceptibility of aged samples was investigated using a doubl...
Published in Journal of Materials Engineering and Performance
The mechanical properties, corrosion resistance and microstructure of the spray-formed 7075 alloy after one-stage aging treatments were studied by using a tensile tester, hardness tester, slow strain rate test, electrical test, intergranular corrosion test, electrochemical corrosion test, scanning electron microscope and transmission electron micro...
Published in Advances in Materials Science
Present paper deals with the influence of a wide range of cold rolling (5, 10, 15 and maximum 40% cold deformation) and the sensitization time (aging at 700°C for 0.12, 0.5, 1, 4, 16 and 32 hours) on intergranular corrosion (IGC). Intergranular corrosion of commercial stainless steel type X6CrNiTi18-10 (1.4541, AISI 321) is frequently observed in s...